Powder XRD (X-Ray Diffraction) Patterns of Dr. A. C. Tas
(ICDD PDF2 Database)


1. Ce4.67(SiO4)3O Hexagonal    (a= 9.6578, c=7.1187 )  43-0441
2. CeAlO3 Tetragonal    (a=3.7630,  c=3.7919 )  48-0051
3. CeAl11O18 Hexagonal    (a=5.55812, c=22.0121 ) 48-0055
4. Ce2SiO5 Monoclinic    (a=9.2780,   b=7.3820, c=6.9560 , b=108.2)      48-0054
5. Ce2Si2O7 Monoclinic    (a=13.0803, b=8.727, c=5.4054 , b=90.134)      48-0058
6. Pr2Si2O7 Monoclinic    (a=13.015, b=8.6717, c=5.4033 , b=90.510)      48-0057
7. Nd2Si2O7 Monoclinic    (a=12.946, b=8.6326, c=5.3908 , b=90.120)      48-0056
8. Sm2Si2O7 Monoclinic    (a=12.8553, b=8.5603, c=5.385 , b=91.470)      48-0053
9. La2Si2O7 Monoclinic    (a=13.1914, b=8.7935, c=5.410 , b=92.060)      48-0052
10. Y Cr0.9 Co0.1 O3 Orthorhombic    (a=7.5202, b=5.514, c=5.2349 )      48-0470
11. Y Cr0.8 Co0.2 O3 Orthorhombic     (a=7.5043, b=5.5039, c=5.2252 )      48-0471
12. Y Cr0.7 Co0.3 O3 Orthorhombic    (a=7.4881, b=5.4952, c=5.2156 )      48-0472
13. Y0.9 Ca0.1 Cr0.9 Co0.1 O3 Orthorhombic     (a=7.5158, b=5.4996, c=5.2411 )      48-0473
14. Y0.9 Ca0.1 Cr0.8 Co0.2 O3 Orthorhombic     (a=7.4963, b=5.4903, c=5.2302 )      48-0474
15. 9Al2O3.2B2O3 Orthorhombic     (a=15.0077, b=7.6850, c=5.3088 ) 53-1233

16.  LaAl(OH(CO3))2 Orthorhombic    (a=8.5945, b=7.4247, c=5.0449 ) 52-1059
17. BaTiO3 Cubic    (a = 4.0186 ) Download
18. Ca10(PO4)6(OH)2 Hexagonal  (a=9.4189, c=6.8827 ) 55-0592

19. GaOOH Orthorhombic (a=4.5545, b=9.8007, c=2.9738 ) 54-0910

20. (La0.8Sr0.2Ga0.8Zn0.2)(OH(CO3))1.867H2O Orthorhombic (a=8.5932, b=7.4085, c=5.0498 ) Download

21. La0.8Sr0.2Ga0.8Zn0.2O2.80 Orthorhombic (a=7.8231, b=5.5310, c=5.5115 ) Download

 

 